Welcome to Nordon Gasket & Packing High Quality Gasket Materials, Seals &
Gaskets for Automobile and Industrial Applications
    Home     |     About us   |     Products      |     Online Inquiry     |     Contact us      |     Site Map
Spiral wound gasket
Ring Joint Gaskets
Non Metallic Gaskets
Gland Packing & Compression Packing
Graphite Sheet Gaskets
Non Asbestos Sheet,Compressed Jointing
Non Asbestos Sheet,Beater Jointing
Asbestos Sheet Compressed Jointing
PTFE & Expanded PTFE
Cylinder Head Gasket Sheet
Rubber Sheet & Roll
Ceramic Fiber and Fibergalss

Nordon Gasket & Packing Co.,LTD.
Address : No.227,Yuping Road,Taohua Industry Park,Hefei 230601,China.
TEL :86-551-63825311
FAX :86-551-63825312
E-mail : info@gasket-material.com
Skype: gasketmaterial

NGP-PC321 Carbonized Fiber Packing
Carbonized fiber packing is a braided packing made of carbonized poly acrylonitrile fiber. It covers wide range of application. For example, it can seal water, brine, factory wastesalt solutions, mineral oil etc. For centrifugal pumps, agitators, mixers, sterntubes etc. What's more, it is relatively economic among non-asbestos packing.

Spec:3.0mm - 50mm


 

table

Pressure

Mpa

2-30

Temperature

íŠ

250

Linear speed

M/s

2-16

PH range

2~12


 


NGP-PC322 Carbonized Fiber Packing with PTFE
It is a braided packing made of carbon fiber which is impregnated with PTFE dispersion. It is inert to almost all corrosive chemicals. When it is used for pumps, frictional heat is freely conducted to the stuffing box metal because of its excellent thermal conductivity, and thus no damage will be caused to the packing. It can replace PTFE asbestos packing within wide service range. It can be used to seal corrosive fluids except strong oxidizer acids, organic solvents, fluids where contamination is not permissible for centrifugal pumps, plunger pumps, mixers valves, etc.
Spec:3.0mm - 50mm


 

table

Pressure

Mpa

2

10

10

Temperature

íŠ

<300

Linear speed

M/s

4

2

2

PH range

0~14


 
NGP-PC320 Carbon Fiber Packing
The carbonized fiber yarn is treated with graphite particles, and then is braided to form packing. Its surface is coated with a high-temperature-proof lubricant. It is able to bear high temperature and pressure, and helps prevent abrasion and also help to minimize the effects of electrolytic pitting of the valve stem.
Spec: 3.0mm - 50mm
Spec:3.0mm - 50mm


 

table

Pressure

Mpa

3

25

25

Temperature

íŠ

<650

Linear speed

M/s

20

2

2

PH range

0~14

 
  NGP-PA321 Acrylic Fiber Graphited Packing
Made from reinforced acrylic fiber, each strand of yarn is sealed off with a special grade of fine graphite flakes. In addition a final coating of graphite is given to final product prior to being squared. A direct replacement for graphite asbestos packing.

Spec:3.0mm - 50mm


 

table

Pressure

Mpa

4

10

15

Temperature

íŠ

260

Linear speed

M/s

10

PH range

2~12

 
NGP-PA320 Acrylic Fiber Packing with PTFE
Made of polyacrylonitrile filament through reinforcing, braiding and impregnated with PTFE, having high strength, wear-and impact -resistance, an ideal substitute for asbestos packings, and applicable for packing seal of pumps, valves and vessels at a high linear speed and pressure.

Spec:3.0mm - 50mm


 

table

Pressure

Mpa

5

10

20

Temperature

íŠ

-100~250

Linear speed

M/s

0~12

PH range

2~12